Influencia del caolín como reemplazo parcial del cemento en la resistencia a compresión axial del concreto de f’c = 210 kg/cm2
Ver/
Descargar
(application/pdf: 277.2Mb)
(application/pdf: 277.2Mb)
Fecha
2018-06-21Autor(es)
Acosta Solano, Eleana Mercedes
Metadatos
Mostrar el registro completo del ítemResumen
RESUMEN
El Caolín es una arcilla, la cual al ser sometida a altas temperaturas tiende a mostrar sus
propiedades puzolánicas. En esta investigación, se presenta la INFLUENCIA DEL CAOLÍN
COMO REEMPLAZO PARCIAL DEL CEMENTO EN LA RESISTENCIA A COMPRESIÓN
AXIAL DEL CONCRETO DE F´c = 210 Kg/cm2, teniendo como objetivo principal:
Determinar la influencia del caolín como reemplazo parcial del cemento en la resistencia a
compresión axial del concreto de f’c = 210 Kg/cm2. El Caolín se extrajo de la cantera de
Llacanora, para luego ser sometido a un horno a elevadas temperaturas, seguido de una
trituración para la obtención de ceniza de Caolín, evidenciándose a través del ensayo
químico de la muestra de caolín realizado que este cumplió con las características para ser
utilizado como material puzolánico. La metodología consistió en realizar probetas de
concreto con f’c de diseño de 210 kg/cm2, reemplazando diferentes porcentajes (5%, 10%
y 15%) de cemento por ceniza de caolín y probetas patrón (sin incorporación de Caolín),
se realizaron los ensayos al concreto en estado fresco y endurecido, siendo el más
importante el concreto en estado endurecido (ASTM C 39). Finalmente se evaluó la
resistencia a compresión axial del concreto a los 7, 14 y 28 días, después del curado
respectivo. En base a los resultados obtenidos al incorporar los diferentes porcentajes de
caolín (5%, 10% y 15%), se pudo observar que al realizar el ensayo a compresión a los 7
días, la resistencia disminuye en 5.53%, 11.01% y 25.95% respectivamente con respecto
a la muestra sin incorporación y en el ensayo realizado a los a los 14 y 28 días, la
resistencia aumenta a los 14 días en 8.84%, 25.76% y 36.97% respectivamente y a los 28
días en 31.91%, 75.71% y 86.88% respectivamente, con respecto a la muestra sin
incorporación, con esto se puede afirmar que la hipótesis planteada si cumple.
Mostrar más
ABSTRACT
Kaolin is a clay, which when subjected to high temperatures tends to show its pozzolanic
properties. In this research, we present the CABLIN INFLUENCE AS PARTIAL
REPLACEMENT OF CEMENT IN THE RESISTANCE TO AXIAL COMPRESSION OF THE
CONCRETE OF F'c = 210 Kg/cm2, having as main objective: To determine the influence of
kaolin as a partial replacement of cement in the resistance to axial compression of the
concrete of f'c = 210 Kg/cm2. The kaolin was extracted from the quarry of Llacanora, and
then subjected to a furnace at high temperatures, followed by a crushing to obtain Kaolin
ash, evidenced by the chemical test of the kaolin sample made that it complied with the
characteristics to be used as pozzolanic material. The methodology consisted of making
concrete specimens with design f'c = 210 kg/cm2, replacing different percentages (5%, 10%
and 15%) of cement by kaolin ash and standard specimens (without incorporation of kaolin).
they carried out tests on concrete in a fresh and hardened state, the most important being
concrete in the hardened state (ASTM C 39). Finally, the resistance to axial compression
of the concrete was evaluated at 7, 14 and 28 days after the respective curing. Based on
the results obtained by incorporating the different percentages of kaolin (5%, 10% and
15%), it was observed that when performing the compression test at 7 days, the resistance
decreases by 5.53%, 11.01% and 25.95 % respectively with respect to the sample without
incorporation and in the test conducted at 14 and 28 days, the resistance increases at 14
days at 8.84%, 25.76% and 36.97% respectively and at 28 days at 31.91%, 75.71% and
86.88% respectively, with respect to the sample without incorporation, with this it is possible
to be affirmed that the hypothesis raised if it is fulfilled.
Mostrar más
Cita bibliográfica
Acosta, E. M. (2017). Influencia del caolín como reemplazo parcial del cemento en la resistencia a compresión axial del concreto de f’c = 210 kg/cm2 (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de http://hdl.handle.net/11537/13481
Materia
Colecciones
- Tesis [1420]
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Influencia de tres niveles de fibra de furcraea andina (penca) sobre la resistencia a la compresión del concreto f’c= 210 kg·cm-²
Zaldivar Vargas, Juan Eduardo (Universidad Privada del Norte, 2018-06-21)Acceso abiertoRESUMEN En la presente tesis se toma énfasis la tecnología del concreto, así como también el uso de materiales no convencionales, para la presente investigación que se usó agregados de la cantera Bazán (carretera ... -
Resistencia mecánica del concreto fc=210 kg/cm² con la adición de fibras de acero dramix y sika
Abanto Cabellos, Oswaldo David (Universidad Privada del Norte, 2018-06-22)Acceso abiertoRESUMEN En la presente tesis, se investigó las propiedades mecánicas del concreto f'c=21 O kgfcm² para lo cual se utilizó los aditivos de fibras de acero, Dramix y Sika, en porcentajes de 1% y 1.5% del peso del agregado ... -
Influencia de la incorporación de fibra de polipropileno monofilamento en la resistencia mecánica del concreto de f’c=210 kg/cm2
Salcedo Espinoza, Wilder Omar (Universidad Privada del Norte, 2017-05-29)Acceso cerradoRESUMEN En la presente investigación se ha evaluado la influencia que tiene la incorporación de fibra de polipropileno monofilamento en la resistencia mecánica del concreto de f´c = 210 kg/cm2. La evaluación consistió ...