Influencia de la aplicación del aditivo Sika Plastiment HE-98 con el fin de mejorar la permeabilidad del concreto, Trujillo 2019
![Thumbnail](/bitstream/handle/11537/22192/Blumen%20Carrera%20Rodrigo%20Alessandro.pdf.jpg?sequence=7&isAllowed=y)
Fecha
2019-08-29Autor(es)
Blumen Carrera, Rodrigo Alessandro
Metadatos
Mostrar el registro completo del ítemResumen
RESUMEN
La presente investigación estudió el comportamiento de un concreto permeable al haberse realizado una mezcla con agregado de ½” y 3/8”, además de un aditivo plastificante, con la finalidad de determinar si el concreto mejora su permeabilidad con ambos agregados.
Para la elaboración de la tesis, se usó cemento Pacasmayo Tipo I, un agregado grueso de tamaño máximo nominal ½” y 3/8”. En total se elaboraron 96 probetas cilíndricas de 10 cm de diámetro y 20cm de altura, 16 probetas fueron elaboradas con agregado de ½” y sin aditivo Sika Plastiment HE-98, 16 con agregado de 3/8” y sin aditivo Sika Plastiment HE-98, 16 con agregado de ½” y con aditivo Sika Plastiment HE-98 al 0.4%, 16 con agregado de 3/8” y con aditivo Sika Plastiment HE98 al 0.4%, 16 con agregado de ½” y con aditivo Sika Plastiment HE-98 al 1.0% y por último 16 con agregado de 3/8” y con aditivo Sika Plastiment HE-98 al 1.0%.
Se evaluó la resistencia a la compresión e infiltración del concreto con dos tipos de agregado grueso, se evaluó la resistencia a compresión del concreto permeable después de un periodo de curado de 3, 7 y 28 días utilizando la Norma ASTM C 39, siendo un total de 72 probetas a ensayar a compresión y en cuanto a la permeabilidad se utilizó la Norma ASTM C 1701 para determinar la cantidad de agua que filtra en un determinado tiempo, para luego con la ecuación proporcionada por la Norma determinar la infiltración en el concreto permeable, siendo un total de 24 probetas a ensayar.
Con los valores obtenidos se analizaron y se determinó que el concreto permeable con agregado de 3/8” con la incorporación de un plastificante mejora la resistencia a compresión y también la permeabilidad en comparación al concreto permeable con agregado de 3/8” sin aditivo plastificante. Sin embargo, el concreto permeable con agregado de ½” disminuyó su resistencia a la compresión, aunque si mejoró la permeabilidad.
Se utilizó el laboratorio de la Universidad Privada del Norte Sede Trujillo para la realización de la presente investigación mediante la elaboración de (probetas) de concreto de 4”x8”, donde se aplicó una estimación puntual para obtener un valor según la muestra estudiada en los ensayos, principalmente se utilizó la herramienta prueba exacta de Fisher de análisis de varianza para estimar un nivel de confianza de 95% en pequeñas muestras, en este caso probetas de concreto sin y con la incorporación del aditivo SIKA Plastiment HE-98.
Mostrar más
ABSTRACT
The present investigation studied the behavior of a permeable concrete to have made a mixture with ½ "and 3/8" aggregate, in addition to a plasticizer additive, in order to determine if the concrete improves its permeability with both aggregates.
For the elaboration of the thesis, Pacasmayo Type I cement was used, a thick aggregate of maximum nominal size ½ "and 3/8". A total of 96 cylindrical test pieces of 10 cm in diameter and 20 cm in height were made, 16 specimens were made with ½ "aggregate and without Sika Plastiment HE-98 additive, 16 with added 3/8" and without Sika Plastiment HE- additive. 98, 16 with ½ "aggregate and with Sika Plastiment HE-98 additive at 0.4%, 16 with added 3/8" and with Sika Plastiment HE-98 additive at 0.4%, 16 with ½ "aggregate and with Sika additive Plastiment HE-98 at 1.0% and finally 16 with added 3/8 "and with additive Sika Plastiment HE-98 at 1.0%.
The compressive strength and infiltration of the concrete was evaluated with two types of coarse aggregate, the compressive strength of the pervious concrete was evaluated after a curing period of 3, 7 and 28 days using the ASTM C 39 Standard, being a total of 72 test specimens to be compressed and in terms of permeability, ASTM C 1701 was used to determine the amount of water that filters in
a given time, and then with the equation provided by the Standard, determine the infiltration in pervious concrete, being a total of 24 test pieces to be tested.
The values obtained were analyzed and it was determined that the pervious concrete with added 3/8 "with the incorporation of a plasticizer improves the compressive strength and also the permeability compared to the pervious concrete with added 3/8" without plasticizer additive. However, pervious concrete with ½ "aggregate decreased its compressive strength, although it did improve permeability.
The laboratory of the Universidad Privada del Norte Sede Trujillo was used to carry out the present investigation through the elaboration of 4 "x8" concrete test pieces, where a point estimate was applied to obtain a value according to the sample studied in the tests, mainly the exact test of Fisher tool was used to estimate a confidence level of 95% in small samples, in this case concrete specimens without and with the incorporation of the additive SIKA Plastiment HE-98.
Mostrar más
Cita bibliográfica
Blumen, R. A. (2019). Influencia de la aplicación del aditivo Sika Plastiment HE-98 con el fin de mejorar la permeabilidad del concreto, Trujillo 2019 (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de http://hdl.handle.net/11537/22192
Colecciones
- Tesis [1536]
El ítem tiene asociados los siguientes ficheros de licencia:
Excepto si se señala otra cosa, la licencia del ítem se describe como info:eu-repo/semantics/openAccess
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Influencia de los aditivos SIKA WT-100, SIKA 1 líquido y SIKA 1 en polvo en la resistencia a la compresión y permeabilidad del concreto, Trujillo, 2018
Benites Bacilio, Percy Oliver; Moreno Carranza, Mirko Jose (Universidad Privada del Norte, 2018-10-18)Acceso abiertoEl presente trabajo de investigación se desarrolló en la ciudad de Trujillo, región la Libertad en el año 2018, teniendo como principal objetivo determinar de qué manera influyen los aditivos impermeabilizantes sika WT-100, ... -
Influencia de la relación agua – cemento, tipo de aditivo impermeabilizante y de cemento en la resistencia a compresión y para la permeabilidad en concreto un estructuras hidráulicas, Trujillo, 2018
Cruz León, Arturo Marcos Guillermo; Medina Romero, Bryan Alexis (Universidad Privada del Norte, 2019-04-22)Acceso abiertoEn la presente tesis de investigación, se evaluó la influencia de las diferentes relaciones agua – cemento, tipos de aditivos impermeabilizantes y tipo de cemento, al ser usados en un concreto para estructuras hidráulicas, ... -
Influencia de los aditivos sika retarder y sikatard en la resistencia a la compresión, asentamiento y tiempo de fraguado de un concreto f'c=210kg/cm2, Trujillo 2021
Quiroz Cerna, Beto Alexis (Universidad Privada del Norte, 2021-03-26)Acceso abiertoLa presente tesis se llevó a cabo en la ciudad de Trujillo, departamento de La Libertad. El fin de esta investigación fue hacer mejoras en las propiedades físicas y mecánicas del concreto como la resistencia a la compresión, ...