dc.identifier.citation | Ramirez, L., & Yupanqui, R. F. (2021). Influencia de la adición de microsilice y del aditivo superplastificante en las propiedades del concreto antideslave, Trujillo 2021 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. https://hdl.handle.net/11537/30455 | es_PE |
dc.identifier.other | 624.1834 RAMI 2021 | es_PE |
dc.identifier.uri | https://hdl.handle.net/11537/30455 | |
dc.description.abstract | La presente investigación tuvo como objetivo determinar la influencia de la adición de
microsílice y del aditivo superplastificante en las propiedades de un concreto antideslave en la
ciudad de Trujillo 2021, para ello se aplicó un diseño experimental puro de tipo bifactorial y
se utilizó como instrumento la guía de observación, el muestreo fue de tipo probabilístico y la
técnica de análisis de datos por estadística descriptiva e inferencial. Se realizó nueve diseños
de mezclas bajo las recomendaciones del ACI 237R-07 para luego evaluar sus propiedades en
estado fresco, tales como capacidad de llenado, capacidad de paso, viscosidad, resistencia a la
segregación y resistencia a la pérdida de finos; en estado endurecido, la resistencia a la
compresión a 7, 28 y 56 días; finalmente, el método de colocación por el sistema tremie. Los
resultados evidencian que, para un diseño óptimo del 15% de microsílice con el 1.25% de
aditivo superplastificante, las mezclas de concreto antideslave presentaron una alta fluidez,
logrando así: una capacidad de llenado de 618 mm, una capacidad de paso de 0.82, una
viscosidad con un tiempo de 14.04 segundos y una resistencia a la segregación con un valor
VSI de 0. Así mismo, manifestaron una gran cohesividad entre sus componentes debido al
escaso porcentaje de pérdida de finos del 1.12%, una mayor resistencia a la compresión de 631
kg/cm2 a los 28 días y, además de lograr una adecuada colocación bajo el agua. Por lo tanto, se
logró determinar la influencia de la adición de microsílice y del aditivo superplastificante en
las propiedades del concreto antideslave. | es_PE |
dc.description.abstract | The objective of the present investigation was to determine the influence of the addition of
microsilica and the superplasticizer additive on the properties of an anti-washout concrete in
the city of Trujillo 2021, for which a pure two-factor experimental design was applied the
observation guide was used as an instrument, the sampling was probabilistic and the data
analysis technique by descriptive and inferential statistics was used. Nine designs of mixtures
were made under the recommendations of ACI 237R-07 to later evaluate their properties in
fresh state, such as filling capacity, flow capacity, viscosity, resistance to segregation and
resistance to loss of fines; in the hardened state, the compressive strength at 7, 28 and 56 days;
finally, the method of placement by the tremie system. The results show that, for an optimal
design of 15% microsilica with 1.25% superplasticizer additive, the anti-washout concrete
mixtures presented high fluidity, thus achieving: a filling capacity of 618 mm, a passage
capacity of 0.82, a viscosity with a time of 14.04 seconds and a resistance to segregation with
a VSI value of 0. Likewise, they showed great cohesiveness between their components due to
the low percentage of loss of fines of 1.12%, a higher compressive strength of 631 kg/cm2 at
28 days and, in addition to achieving adequate placement under water. Therefore, it was
possible to determine the influence of the addition of microsilica and the superplasticizer
additive on the properties of the anti-washout concrete. | es_PE |
dc.description.uri | Tesis | es_PE |
dc.format | application/pdf | es_PE |
dc.format | application/msword | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Privada del Norte | es_PE |
dc.rights | info:eu-repo/semantics/openAccess | es_PE |
dc.rights | Atribución-NoComercial-CompartirIgual 3.0 Estados Unidos de América | * |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-sa/3.0/us/ | * |
dc.source | Universidad Privada del Norte | es_PE |
dc.source | Repositorio Institucional - UPN | es_PE |
dc.subject | Concreto | es_PE |
dc.subject | Mezcla | es_PE |
dc.subject | Aditivos | es_PE |
dc.subject | Microsílice | es_PE |
dc.subject | Superplastificante | es_PE |
dc.subject | Materiales de construcción | es_PE |
dc.title | Influencia de la adición de microsilice y del aditivo superplastificante en las propiedades del concreto antideslave, Trujillo 2021 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.grantor | Universidad Privada del Norte. Facultad de Ingeniería | es_PE |
thesis.degree.level | Título Profesional | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.01 | es_PE |
thesis.degree.program | Pregrado | es_PE |
dc.description.sede | Trujillo San Isidro | es_PE |
renati.advisor.dni | 40385695 | |
renati.advisor.orcid | https://orcid.org/0000-0001-9018-5763 | es_PE |
renati.author.dni | 70164589 | |
renati.author.dni | 73086248 | |
renati.discipline | 732016 | es_PE |
renati.juror | Alvarado Ruiz, Cinthya | |
renati.juror | Azañedo Medina, Wiston | |
renati.juror | Sagástegui Vásquez, Germán | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | http://purl.org/pe-repo/renati/type#tesis | es_PE |