Análisis de las propiedades físico – mecánicas del concreto permeable con adición de gel de aloe vera y escoria de acero en reemplazo parcial del cemento para pavimentos rígidos, Lima 2023
Ver/
Investigación pdf
(application/pdf: 7.682Mb)
(application/pdf: 7.682Mb)
Investigación docx
(application/vnd.openxmlformats-officedocument.wordprocessingml.document: 23.45Mb)
Embargado hasta el 01/07/2074
(application/vnd.openxmlformats-officedocument.wordprocessingml.document: 23.45Mb)
Embargado hasta el 01/07/2074
Fecha
2023-11-08Autor(es)
Chavez Alcala, Jimmy Andree
Medianero Bazan, Keller Cesar
Metadatos
Mostrar el registro completo del ítemResumen
En la investigación realizada se tiene como objeto de estudio la determinación de las propiedades físico-mecánicas del concreto permeable adicionando gel de aloe vera y escoria de acero en reemplazo parcial del cemento para pavimentos rígidos Lima 2023, la investigación es de tipo experimental, diseño cuasi-experimental y el enfoque cuantitativo para esto se desarrollaron diseños del concreto permeable con adición al 3, 5 y 7% de gel de aloe vera y al 4 y 8% de escoria de acero y luego obtener sus propiedades físico-mecánicas, a continuación se mencionan los resultados; en el aspecto de las propiedades físicas el diseño de mejores características fue el de 5% G.A.V. + 8% E.A., donde se obtuvo un asentamiento de 1/2” y una relación agua cemento de 0.56. En el esfuerzo a la compresión se obtuvo que el diseño de mayor eficacia fue el de 5% G.A.V. + 8% E.A., a los 28 días se logró un 232.4 kg/cm2, en comparación con el concreto patrón tuvo una mejora del 8%. En el esfuerzo a la flexión se obtuvo que el diseño de mayor eficacia fue el de 5% G.A.V. + 8% E.A., a los 28 días se logró un 32.4 kg/cm2, en comparación con el concreto patrón tuvo una mejora del 8%. En el ensayo de permeabilidad se obtuvo que el de mayor eficacia fue el diseño de 7% G.A.V. + 4% E.A., a los 28 días se logró un coeficiente de permeabilidad 9.53 mm/s, en comparación con el concreto patrón a 28 días se tuvo una mejora del 22%. También se concluyó estadísticamente y con un nivel de significancia del 5% que al adicionar el 5% G.A.V. + 8% E.A., se eleva significativamente el esfuerzo a la compresión y Flexion, y en el caso de la permeabilidad el diseño con el 7% G.A.V. + 4% E.A., se eleva significativamente en el coeficiente de permeabilidad, mientras que en los demás diseños el aumento de las medias no es significativo, son similares o menores al diseño patrón.
Mostrar más
The research carried out has as its object of study the determination of the physical-mechanical properties of permeable concrete by adding aloe vera gel and steel slag in partial replacement of cement for rigid pavements Lima 2023, the research is experimental, quasi-design. -experimental and quantitative approach for this, designs of permeable concrete were developed with the addition of 3, 5 and 7% of aloe vera gel and 4 and 8% of steel slag and then obtained their physical-mechanical properties, below. they mention the results; In terms of physical properties, the design with the best characteristics was the one with 5% G.A.V. + 8% E.A., where a settlement of 1/2” and a water-cement ratio of 0.56 were obtained. In the compressive stress, it was found that the most effective design was that of 5% G.A.V. + 8% E.A., after 28 days 232.4 kg/cm2 was achieved, compared to the standard concrete it had an improvement of 8%. In the bending effort, it was found that the most effective design was the 5% G.A.V. + 8% E.A., after 28 days 32.4 kg/cm2 was achieved, compared to the standard concrete it had an improvement of 8%. In the permeability test, it was found that the most effective design was the 7% G.A.V. + 4% E.A., at 28 days a permeability coefficient of 9.53 mm/s was achieved, compared to the standard concrete at 28 days there was an improvement of 22%. It was also concluded statistically and with a significance level of 5% that by adding 5% G.A.V. + 8% E.A., the compression and flexion stress is significantly increased, and in the case of permeability the design with 7% G.A.V. + 4% E.A., the permeability coefficient increases significantly, while in the other designs the increase in the means is not significant, they are similar or lower than the standard design.
Mostrar más
Cita bibliográfica
Chavez, J. A., & Medianero, K. C. (2023). Análisis de las propiedades físico – mecánicas del concreto permeable con adición de gel de aloe vera y escoria de acero en reemplazo parcial del cemento para pavimentos rígidos, Lima 2023 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. https://hdl.handle.net/11537/36974
Materia
Colecciones
- Tesis [1476]
El ítem tiene asociados los siguientes ficheros de licencia:
Excepto si se señala otra cosa, la licencia del ítem se describe como info:eu-repo/semantics/openAccess
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Adición de porcentajes al 16%, 32% y 48 % de concreto reciclado al diseño de pavimento rígido para mejorar las propiedades de físico mecánicas, Lima 2022
Mallqui Matienzo, Bryan Adrian (Universidad Privada del Norte, 2023-04-12)Acceso abiertoEl objetivo de la presente investigación es determinar la influencia de la adición de porcentajes al 16%, 32% y 48 % de concreto reciclado en la mejora de las propiedades de físico mecánicas del diseño de pavimento rígido, ... -
Influencia de los aditivos SIKA WT-100, SIKA 1 líquido y SIKA 1 en polvo en la resistencia a la compresión y permeabilidad del concreto, Trujillo, 2018
Benites Bacilio, Percy Oliver; Moreno Carranza, Mirko Jose (Universidad Privada del Norte, 2018-10-18)Acceso abiertoEl presente trabajo de investigación se desarrolló en la ciudad de Trujillo, región la Libertad en el año 2018, teniendo como principal objetivo determinar de qué manera influyen los aditivos impermeabilizantes sika WT-100, ... -
Influencia de la granulometría del agregado grueso en las propiedades mecánicas e hidráulicas de un concreto permeable, Trujillo 2017
Perez Gordillo, Johan Joe (Universidad Privada del Norte, 2017-11-13)Acceso abiertoRESUMEN La investigación realizada se centra en el análisis del efecto que tiene la variación de la granulometría del agregado grueso en las propiedades mecánicas e hidráulicas de un concreto permeable. Las propiedades ...