Influencia de la adición de la ceniza de pepa de pino y eucalipto en las propiedades físico-mecánicas de un concreto 210 kg/cm2 para el diseño de vigas, columnas. Cajamarca – 2023
View/ Open
Investigación pdf
(application/pdf: 29.01Mb)
(application/pdf: 29.01Mb)
Investigación docx
(application/vnd.openxmlformats-officedocument.wordprocessingml.document: 70.86Mb)
Embargado hasta el 02/07/2074
(application/vnd.openxmlformats-officedocument.wordprocessingml.document: 70.86Mb)
Embargado hasta el 02/07/2074
Date
2024-04-16Author(s)
Chavez Marin, Edson Denis
Ochoa Condor, Clinton Jhon
Metadata
Show full item recordAbstract
El presente trabajo de investigación tiene como objetivo determinar la influencia en las propiedades físico-mecánicas del concreto f’c=210 kg/cm² al adicionar en 1%, 3% y 5% por ceniza de pepa de eucalipto y 1%, 3% y 5% ceniza de pepa de pino para el diseño de vigas y columnas. Cajamarca – 2023. Para el desarrollo del trabajo se optó por la elaboración de 10 diseños, de las cuales 9 son en combinaciones de ceniza de 1%, 3% y 5% de pepa de pino y 1%, 3% y 5% de pepa de eucalipto y un diseño patrón. La metodología aplica en la investigación fue de tipo de investigación aplicada, enfoque cuantitativo, de nivel explicativo y de diseño cuasi experimental. Por lo tanto, la población está establecido por 210 testigos de concreto, de los cuales son 90 probetas de forma cilíndrica de 15x30 cm; 30 viguetas de concreto de 15x15x50 cm y 90 cubos de 5x5x5 cm, las cuales fueron ensayadas a los 7, 14 y 28 días de curado para obtener resultados de la resistencia a la compresión, flexión y desgaste por abrasión. Obtenido como resultados a los 28 días de un concreto optimo con las combinaciones de 5%CPP Y 5%CPE, 243 kg/cm2 de resistencia a la compresión, 31.45 kg/cm2 de resistencia a la flexión y 18.6 gr de desgaste por abrasión del concreto a diferencia que de un concreto patrón con desgaste de 29 gr. Llegando a concluir que la temperatura y la trabajabilidad influyen positivamente. De tal manera del análisis de resultados del concreto endurecido, se puede decir que al adicionar las cenizas de pepa de pino y eucalipto mejoran significativamente la resistencia a compresión, flexión y desgaste por abrasión con respecto a un concreto patrón f´c=210kg/cm2.
Mostrar más
The purpose of this research work is to determine the influence on the physical-mechanical properties of concrete f'c=210 kg/cm² by adding 1%, 3% and 5% eucalyptus seed ash and 1%, 3% and 5% pine seed ash for the design of beams and columns. Cajamarca - 2023. For the development of the work, 10 designs were chosen, of which 9 are in combinations of 1%, 3% and 5% pine needle ash and 1%, 3% and 5% eucalyptus needle ash and a standard design. The methodology applied in the research was applied research type, quantitative approach, explanatory level and quasi-experimental design. Therefore, the population is established by 210 concrete samples, of which 90 are cylindrical specimens of 15x30 cm; 30 concrete beams of 15x15x50 cm and 90 cubes of 5x5x5 cm, which were tested at 7, 14 and 28 days of curing to obtain results of resistance to compression, bending and wear by abrasion. Obtained as results at 28 days of an optimum concrete with the combinations of 5%CPP and 5%CPE, 243 kg/cm2 of compressive strength, 31.45 kg/cm2 of flexural strength and 18.6 gr of wear by abrasion of the concrete as opposed to a standard concrete with wear of 29 gr. It was concluded that temperature and workability have a positive influence. From the analysis of the results of the hardened concrete, it can be said that the addition of pine and eucalyptus seed ashes significantly improves the compressive strength, flexural strength and abrasive wear with respect to a standard concrete f'c=210kg/cm2.
Mostrar más
Bibliographic citation
Chavez, E. D., & Ochoa, C. J. (2023). Influencia de la adición de la ceniza de pepa de pino y eucalipto en las propiedades físico-mecánicas de un concreto 210 kg/cm2 para el diseño de vigas, columnas. Cajamarca – 2023 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. https://hdl.handle.net/11537/36978
Subject
Collections
- Tesis [1476]
The following license files are associated with this item:
Related items
Showing items related by title, author, creator and subject.
-
Resistencia a la compresión del concreto f’c= 210 Kg/cm2 con la adición de diferentes porcentajes de ceniza de bagazo de caña de azúcar, UPNC 2016
Jiménez Chávez, Geoffrey Andreé (Universidad Privada del Norte, 2016-06-01)Acceso abiertoRESUMEN En el desarrollo de la presente investigación se ha determinado la influencia en la resistencia a la compresión de concreto f´c= 210 Kg/cm 2 usando agregados de la cantera Roca fuerte con la adición de la ... -
Resistencia a la compresión del concreto fʹc=210 kg/cm2 para pavimento rígido, optimizando la abrasión del agregado grueso de las canteras Roca Fuerte y La Arenita, Cajamarca 2023
Arevalo Ticlla, Christian Adrian (Universidad Privada del Norte, 2023-10-11)Acceso abiertoLa presente investigación, se desarrolló con el objetivo de determinar la resistencia a la compresión del concreto fˈc = 210 kg/cm2 para pavimento rígido, optimizando la abrasión del agregado grueso de las canteras Roca ... -
Resistencia a la compresión, flexión y abrasión de un concreto f’c 210 kg/cm2 con adición de vidrio molido y piedra pómez en reemplazo parcial del agregado fino y grueso, Lima 2022
Reyes Rondon, Francois Khushall Jules (Universidad Privada del Norte, 2023-08-06)Acceso abiertoLa presente investigación tuvo como uno de sus principales objetivos el poder determinar cuánto resiste un diseño f’c 210 kg/cm2 patrón a la compresión, flexión y abrasión del concreto y el concreto modificado adicionando ...