Influencia de piedra pómez sobre asentamiento, densidad, absorción y resistencia a compresión en concreto liviano estructural
Ver/
Descargar
(application/pdf: 19.23Mb)
(application/pdf: 19.23Mb)
Fecha
2017-05-05Autor(es)
Tantaquilla Cueva, Cleiser Alejandro
Metadatos
Mostrar el registro completo del ítemResumen
RESUMEN
La investigación se enfocó en la obtención de Concretos livianos estructurales compuesto
por un agregado liviano natural como la piedra pómez. Para lograr tal fin se procedió a
realizar una mezcla patrón de concreto convencional con agregados naturales de las
canteras existentes en Huanchaco - Trujillo y otro concreto liviano con el uso de piedra
pómez encontradas en la costa norte del mar peruano, el uso de esta piedra se hizo en
diferentes tamaños 12.50 mm (1/2”), para el agregado grueso y 2.36mm (N°8), para el
agregado fino, para ambos casos el reemplazo de los agregados se dio de acuerdo a las
volúmenes que ocupaban en la mezcla en los siguientes porcentajes 20%, 40%, 60%, 80%
y 100%. Asimismo, se utilizó el cemento portland Tipo ICo y un aditivo superplastificante
EUCO 37 al 1% del contenido del cemento.
Tanto a los agregados livianos y convencionales, se les realizaron los ensayos de
caracterización bajo las Normas ASTM, los cuales fueron requeridos para efectuar los
diseños de mezcla de concreto bajo la norma ACI 211. Se conformaron probetas de 100
x 200 mm (4 x 8 in) de acuerdo a la norma ASTM C192. Se utilizó 4 réplicas por cada
variable para obtener una confiabilidad del 95 %. La resistencia a la compresión se realizó
de acuerdo a la ASTM C39, la densidad bajo la ASTM C642 y ASTM C567, en cuanto al
asentamiento se desarrolló de acuerdo a la ASTM C143.
En el caso del concreto convencional, se estudiaron mezclas de concreto con relación a/c
de 0.583 para una resistencia de 210 kg/cm2
, obteniendo resistencias a la compresión
promedio de 296 kg/cm2 a los 28 días de curado y 323 kg/cm2 a los 56 días de curado, la
densidad promedio de 2263 kg/m3 y un asentamiento de 7.55“. Además un costo de S/.
236.60 por m3
.
Por otro lado, el reemplazo óptimo del agregado grueso por piedra pómez se encuentra en
el rango de 20% a 60% en volumen, obteniendo valores de resistencia a compresión de
276 kg/ cm2 a 233 kg/cm2 a 28 días de curado y 303 kg/cm2 a 259 kg/cm2 a 56 días de
curado. Asimismo un asentamiento de 6.4” a 4” y una densidad de equilibrio de 2150 kg/m3
a 1918 kg/m3
. Además un costo de producción de S/. 238.02 a S/. 240.84 por m3
.
En cuanto al agregado fino el reemplazo óptimo puede ser en hasta un 100%, obteniendo
un valor de resistencia a compresión de 222 kg/cm2 a 28 días de curado y 238 kg/cm2 a 56
días de curado. Asimismo un asentamiento de 5.2” y una densidad de equilibrio de 1956
kg/m3
. Además un costo de producción de S/. 242.73 por m3.
Mostrar más
ABSTRACT
The research project focused on obtaining Lightweight Structural Concrete composed of a
lightweight natural aggregate such as pumice stone. To achieve this aim, a conventional
concrete mix was made with natural aggregates from the existing quarries in Huanchaco -
Trujillo and another light concrete with the use of pumice found on the north coast of the
Peruvian sea, the use of this stone was Made in different sizes 12.50 mm (1/2 "), for the
coarse aggregate and 2.36 mm (No. 6), for the fine aggregate, for both cases the
replacement of the aggregates was given according to the volumes they occupied in the
Mixing in the following percentages: 20%, 40%, 60%, 80% and 100%. Likewise, Type ICo
cement and EUCO 37 superplasticizer additive were used at 1% of the cement content.
Both the light and conventional aggregates were subjected to characterization tests under
ASTM Standards, which were required to perform the concrete mix designs under ACI 211.
Samples of 100 x 200 mm (4 x 8 in) were made according to Standard ASTM C192. Four
replicates were used for each variable to obtain a reliability of 95%. Compressive strength
was performed according to ASTM C39, density under ASTM C642 and ASTM C567, as
far as settling was developed according to ASTM C143.
In the case of conventional concrete, concrete mixtures were studied in relation to a / c of
0.58 for a strength of 210 kg/cm2
, obtaining average compressive strengths of 296 kg/cm2
at 28 days of curing and 323 kg/cm2
. At 56 days of curing, the average density of 2263
kg/m3 and a settlement of 7.55”. In addition, a cost of S /. 236.60 per m3.
On the other hand, the optimum replacement of the thick aggregate by pumice is in the
range of 20% to 60% by volume, obtaining compressive strength values from 276 kg/cm2
to 233 kg/cm2 at 28 days of curing and 303 kg/cm2 at 259 kg / cm 2 at 56 days of curing.
Also a settlement of 6.4 "to 4" and an equilibrium density of 2150 kg / m3 to 1918 kg/m3
. In
addition, a production cost of S/. 238.02 and S/. 240.84 per m3.
As for the fine aggregate the optimum replacement can be up to 100%, obtaining a
compressive strength value of 222 kg/cm2 at 28 days of curing and 238 kg/cm2 at 56 days
of curing. Also a settlement of 5.2 "and an equilibrium density of 1956 kg/m3
. In addition, a
production cost of S/. 242.73 per m3.
Mostrar más
Cita bibliográfica
Tantaquilla, C. A. (2017). Influencia de piedra pómez sobre asentamiento, densidad, absorción y resistencia a compresión en concreto liviano estructural (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de http://hdl.handle.net/11537/12533
Colecciones
- Tesis [1436]
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Influencia de la densidad de las perlas de poliestireno sobre el costo, peso unitario, asentamiento, resistencia a compresión y flexión en un concreto ligero estructural para losas aligeradas, Trujillo 2020
Chuquizapon Suarez, Kevin David; Ibañez Moreno, Christian Ayrton Max (Universidad Privada del Norte, 2020-09-16)Acceso abiertoLa presente tesis fue realizada en la ciudad de Trujillo, donde se realizaron los ensayos en el laboratorio de concreto de la Universidad Privada del Norte, y tuvo como objetivo principal determinar la influencia de la ... -
Resistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto reciclado
Rodríguez Cabanillas, Gianmarco (Universidad Privada del Norte, 2018-09-05)Acceso abiertoRESUMEN La presente tesis tiene como objetivo determinar la resistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto reciclado. Para este estudio se utilizó ... -
Medición de las propiedades geoquímicas y mecánicas del pasivo ambiental relave Mina Paredones para su propuesta de utilización como relleno en pasta para labores mineras subterráneas - Cajamarca, setiembre 2015
Benites Mostacero, Rogger Hans; Leiva Cercado, Yanet (Universidad Privada del Norte, 2015-06-01)Acceso abiertoRESUMEN La presente tesis hace referencia al estudio de los parámetros geoquímicos y mecánicos del relave minero que se tiene acumulado en la relavera de la Mina Paredones, para su posible aplicación como relleno en pasta ...