dc.contributor.advisor | Vásquez Alfaro, Iván Eugenio | |
dc.contributor.author | Velarde Rubio, Alfredo Ruggeri | |
dc.date.accessioned | 2018-02-10T15:51:10Z | |
dc.date.available | 2018-02-10T15:51:10Z | |
dc.date.issued | 2017-12-14 | |
dc.identifier.citation | Velarde, A. R. (2017). Evaluación del polvo de aluminio fundido sobre el asentamiento, compresión, densidad, absorción en un concreto ligero, Trujillo-2017 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. https://hdl.handle.net/11537/12744 | es_PE |
dc.identifier.other | 624.1834 VELA 2017 | es_PE |
dc.identifier.uri | https://hdl.handle.net/11537/12744 | |
dc.description.abstract | En la presente tesis de grado, se investigó el comportamiento del polvo de aluminio en concreto
ligero para la construcción de losas aligeradas sobre su resistencia a la compresión, asentamiento,
absorción, densidad y tiempo de fraguado, se logra obtener por procesos de material espumoso e
incorporador de aire hacen un concreto ligero con una densidad no mayor a 1900 kg/m
, para la
presente investigación, se añadió polvo de aluminio lo que pasa de la malla N°40 (0.425mm) al
1.5%,3%,4.5% y 6% del peso del cemento, sin superplastificante y con superplastificante al 1%, se
obtuvo de la empresa Química Suiza Industrial EUCO 37. El concreto se diseñó para 210 kg/cm
a
base de Cemento Portland Compuesto Tipo ICo de la empresa Pacasmayo, arena y piedra de 3/8”
de la cantera “Los Mellizos” en el distrito de Huanchaco, una relación agua/cemento constante de
0.55 y polvo de aluminio (Al) obtenido del reciclado de pistones de carros es un tipo de aluminio
fundido, en el Emporio Albarracín, Urb. Palermo, Trujillo. Se conformaron probetas cilíndricas de 10
cm de diámetro y 20 cm de alto; curadas a los 28 días en una poza con hidróxido de calcio (NTP
339.183). Para determinar su resistencia a la compresión se empleó la norma NTP 339.034, para el
asentamiento la NTP 339.035 y la NTP 339.187 para absorción y densidad, para el tiempo de
fraguado NTP 339.082. Con la aplicación del polvo de aluminio en el concreto, se produjo un
concreto menos pesado, pero aumentando su grado de absorción y a su vez manteniendo el
asentamiento y su resistencia a la compresión. El diseño patrón o mezcla con 0% de polvo de
aluminio y sin superplastificante alcanzó una resistencia a la compresión de 224 kg/cm
, un
asentamiento de 4”, una absorción de 2.22% y densidad de 2268 kg/m
3
. El diseño más óptimo del
concreto ligero se dio al 1.5% de polvo de aluminio con superplastificante en base a los ensayos
realizados durante esta investigación, presentándose un valor de resistencia de 236 kg/cm
,
asentamiento de 4”, absorción de 3.07% y densidad de 1765.55 kg/m
3
. Mientras que para el concreto
añadiendo polvo de aluminio de 1.5% del peso de cemento sin superplastificante se obtuvo una
resistencia de 195 kg/cm
2
, un asentamiento de 3 ¼”, una absorción de 4.32% y una densidad de
1783 kg/m
3
. El costo aproximado de hacer una mezcla para concreto ligero es de S/. 250.51. Al
utilizar concreto ligero en cualquier tipo de estructura se aprecian cargas muertas mucho más
livianas, importante en áreas de alto riesgo sísmico. La baja densidad del concreto ligero, asegura
a las estructuras de concreto. Durante un sismo las edificaciones no serán afectadas gravemente,
de está manteniendo a la población más segura durante el acontecimiento de un terremoto de gran
intensidad. | es_PE |
dc.description.abstract | The research project, we investigate the behavior of aluminum powder in lightweight concrete for the
construction of lightened slabs on their resistance to compression, settlement, absorption, density
and time of fragmentation, it is obtained by processes of foamy material and The air lift has a light
weight with a density not higher than 1900 kg / m
3
, for the present investigation, aluminum powder
was added as it passes from the mesh No. 40 (0.425 mm) to 1.5%, 3%, 4.5 % and 6% of the weight
of the cement, without superplasticizer and with 1% superplasticizer, was obtained from the company
Química Suiza Industrial EUCO 37. The concrete was designed for 210 kg / cm
2
based on Type ICo
cement of the company Pacasmayo, sand and stone of 3/8 "from the" Los Mellizos "quarry in the
district of Huanchaco, a constant water / cement ratio of 0.55 and aluminum powder (Al) obtained
from the recycling of car pistons is a type of molten aluminum, in the Emp ori or Albarracín, Urb.
Palermo, Trujillo. Cylindrical specimens of 10 cm in diameter and 20 cm in height were formed; cured
at 28 days in a well with calcium hydroxide (NTP 339.183). To determine its resistance to
compression, the NTP 339.034 standard was used for the settlement of NTP 339.035 and NTP
339.187 for absorption and density, for setting time NTP 339.082. With the application of aluminum
powder in concrete, but with a higher degree of absorption and in turn maintaining the settlement
and its resistance to compression. The standard design or mixture with 0% aluminum powder and
without superplasticizer achieved a compressive strength of 224 kg / cm
2
, a 4 "setting, an absorption
of 2.22% and a density of 2268 kg / m
3
of the concrete to 1.5% of aluminum powder with
superplasticizer based on the tests made for this investigation, presenting a resistance value of 236
kg / cm
2
, settlement of 4 ", absorption of 3.07% and density of 1765.55 kg / m
While aluminum
powder could be added to 1.5% by weight of the cement without superplasticizer, a resistance of 195
kg / cm
2
, a settlement of 3 ¼ ", an absorption of 4.32% and a density of 1783 kg / m
The approximate
cost of making a mix for a single floor is S / .250.51 Someone lightweight in any type of structure can
see much lighter dead loads, important in areas of high seismic risk The low density of lightweight
concrete , assures the concrete structures, during an earthquake the buildings have not become
serious, of being in the safest population during the event of a high intensity earthquake. | es_PE |
dc.description.uri | Tesis | es_PE |
dc.format | application/pdf | es_PE |
dc.format | application/msword | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Privada del Norte | es_PE |
dc.rights | info:eu-repo/semantics/openAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-sa/3.0/us/ | * |
dc.source | Universidad Privada del Norte | es_PE |
dc.source | Repositorio Institucional - UPN | es_PE |
dc.subject | Aluminio | es_PE |
dc.subject | Resistencia a la comprensión | es_PE |
dc.subject | Concreto | es_PE |
dc.title | Evaluación del polvo de aluminio fundido sobre el asentamiento, compresión, densidad, absorción en un concreto ligero, Trujillo-2017 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.grantor | Universidad Privada del Norte. Facultad de Ingeniería | es_PE |
thesis.degree.level | Título Profesional | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.01 | es_PE |
thesis.degree.program | Pregrado | es_PE |
dc.description.sede | Trujillo San Isidro | es_PE |
renati.advisor.dni | 80524374 | |
renati.advisor.orcid | https://orcid.org/0000-0002-6717-0501 | es_PE |
renati.author.dni | 73359827 | |
renati.discipline | 732016 | es_PE |
renati.juror | Vásquez Díaz, Alberto Rubén | |
renati.juror | Fernández Fernández, Carlos Humberto | |
renati.juror | Ramírez Mercado, Roger Estuardo | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |