Resistencia mecánica del concreto fc=210 kg/cm² con la adición de fibras de acero dramix y sika
View/ Open
Descargar
(application/pdf: 53.19Mb)
(application/pdf: 53.19Mb)
Date
2018-06-22Author(s)
Abanto Cabellos, Oswaldo David
Metadata
Show full item recordAbstract
RESUMEN
En la presente tesis, se investigó las propiedades mecánicas del concreto f'c=21 O
kgfcm² para lo cual se utilizó los aditivos de fibras de acero, Dramix y Sika, en
porcentajes de 1% y 1.5% del peso del agregado fino. Inicialmente se determinó las
propiedades del agregado grueso y agregado fino los cuales fueron obtenidos de la
cantera "Chancadora Bazán", con estos datos se realizó un diseño de mezcla patrón.
Obtenida la dosificación del diseño de mezcla, en laboratorio se elaboraron probetas
de .concreto, .con .cemento .portland lipa :1, Ias .cuales fueron tOS .probeías .para .el
ensayo de resistencia a compresión axial a edades de 7, 14 Y 28 días, así como 35
prismas rectangulares para los ensayos de flexión en los tercios de la luz y 35
probetas circulares para el ensayo de tracción indirecta por compresión diametral,
estos ríos 'últirrrtrs 'ffilsayos -a"edades ríe '28 rítas.
Obteniendo los resultados del ensayo a compresión axial, el concreto patrón a los 28
días fue de 218.04 kgfcm2, llegó a cumplir con la resistencia de diseño, la mayor
resistencia se obtuvo con la adición de 1.5% de fibras de acero Dramix, la cual llego a
una resistencia de 298.22 kgfcm², llegando aumentar en un 40% resistencia para la
cual fue de diseñada. El resultado del ensayo a flexión en los tercios de la luz, está
cumpliendo con lo establecido en la norma NTP 339.078, el módulo de rotura del
concreto patrón fue de 34.39 kg/cm2, por lo que fue el óptimo, sin embargo, el concreto
con adición de fibras de acero Dramix logro aumentar un 2% el módulo de rotura ya
que llego a 46.20 Kg/cm². Al igual que el ensayo anterior, el ensayo de resistencia a
tracción por compresión diametral, está cumpliendo con lo establecido en la norma
NTP 3.3.a.084.debído a _qu.e.el concreto .patrón .así .como .et .concreto .con .adición ríe
fibras de acero DRAMIX y SIKA su módulo de rotura fueron de 22.57 kgfcm²,
29.34 kgfcm² y 28.56 kgfcm² respectivamente, por lo que se encuentran dentro de lo
establecido por la NTP 339.078, llegando a la conclusión que la hipótesis se cumple
-p-arciaimente rrebido a que elensayo de compresión axial fue -el único que rnostro un
aumento mayor al 15% de la resistencia final.
Mostrar más
ABSTRACT
In the present thesis, the mechanical properties of the concrete f'c = 210 kg/cm² were
investigated, for which the additives of steel fibers, Dramix and Sika, in percentages of
1% and 1.5%of the weight were used. of the fine qggre_fJate.lnitially the .properties of
the coarse aggregate and fine aggregate were determined, which were obtained from
the quarry "Chancadora Bazán", with this data a pattern mix design was made. Once
the mixing design was dosed, in the laboratory, concrete samples were made with
-¡:>ortlana'cernent -ty¡:>e -1, -whicAwere ~·05 ·test -pieees ter ·the -a~dal-oempreesien
resistance test at the ages of 7, 14 and 28 days, as well as 35 rectangular prisms for
the tests of flexion in the thirds of the light and 35 circular specimens for the indirect
tensile test by diametral compression, these last two tests at ages of 28 days.
-Obtairiing{he resúlts of the axial cornpression test, ths standard concrete al 2"8days
was 218.04 kg/cm², it came to comply with the design resistance, the highest
resistance was obtained with the addition of 1.5%fibers of Dramix steel, which reached
a resistance of 298.22 kg/cm², increasing by 40% resistance for which it was
designed. The result of the test to flexion in the thirds of the light, is complying with the
established in the norm NTP 339.078, the modulus of breakage of the concrete pattern
was of 34.39 kg I cm2, so it was the optimum, however, the concrete With the addition
of Dramix steel fibers, I mana_gedto increase the breakin_fJmodulus by 2%, since it
reached 46.20 Kg I cm². Like the previous test, the test of tensile strength by diametral
compression, is complying with the established in the norm NTP 339.084 because the
concrete pattern as well as the concrete with addition of steel fibers DRAMIX y SIKA
its -ffio€Julus -ef rupture wer-e 22.51' icgfcm², 2-9.34 1(:gfcm² 'sAd 28.56 -k:gfc'm²
respectively, so they are within the established by the NTP 339.078, reaching the
conclusion that the This hypothesis is partially fulfilled because the axial compression
test was the only one that showed an increase greater than 15% of the final resistance.
Mostrar más
Bibliographic citation
Abanto, O. D. (2017). Resistencia mecánica del concreto fc=210 kg/cm² con la adición de fibras de acero dramix y sika (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de http://hdl.handle.net/11537/13479
Collections
- Tesis [1566]
Related items
Showing items related by title, author, creator and subject.
-
Comparación de la resistencia a la flexión que alcanza el concreto reforzado con fibras de acero con respecto al concreto tradicional para pavimentos rígidos, 2016
Cusquisiván Chilón, Manuel Edgar; Sáenz Correa, Jean Pier (Universidad Privada del Norte, 2016-05-20)Acceso abiertoEn la presente investigación se realizó la comparación de la resistencia a la flexión de concreto de diseño para un f´c = 210 kg/cm2 y 280 Kg/cm2, respectivamente; las mismas que fueron consideradas como ... -
Influencia de la adición de fibra de acero y plastificante en la resistencia a la compresión del concreto convencional, Trujillo -2018
Castañeda Muñoz, Raúl Exgardo (Universidad Privada del Norte, 2018-07-17)Acceso abiertoLa investigación realizada se centra en el análisis de la influencia de la fibra de acero y aditivo plastificante en la resistencia a la compresión de un concreto convencional. Las dosificaciones de la fibra de acero que ... -
Efectos de las fibras de polipropileno sobre las propiedades físico mecánico de un concreto convencional para pavimentos rígidos utilizando cemento Qhuna, Trujillo - La Libertad 2018
Silupu Tello, Hussein Jose; Saldaña Briones, Jhonnatan Frank (Universidad Privada del Norte, 2019-02-26)Acceso abiertoRESUMEN La presente investigación se desarrolló en la ciudad Trujillo, en las instalaciones de la Universidad Privada del Norte – Laboratorio de Concreto y Estructuras. de tal manera la investigación tuvo como propósito ...