Influencia en la resistencia a la compresión del concreto convencional al sustituir agregado fino por plástico Pet y caucho de llantas recicladas

Thumbnail
View/Open
Descargar
(application/pdf: 467.1Kb)
Embargado
(application/pdf: 566.3Kb)
Embargado hasta el 20/02/2070
Embargado
(application/pdf: 558.8Kb)
Embargado hasta el 20/02/2070
Date
2018-07-23
Author
Miranda Mego, Jary Leyneker
Quispe Boado, Ángel Alberto
Metadata
Show full item record
Abstract
La presente investigación tuvo como objetivo calcular la influencia en la resistencia a la compresión de un concreto convencional al sustituir agregado fino por plástico PET y caucho de llantas recicladas. La sustitución es en volumen al 0%, 5%, 10% y 15%. Para ello se realizó un diseño de mezcla patrón para obtener un concreto convencional de 175 kg/cm², a base de Cemento Portland Compuesto Tipo I Co de la empresa Pacasmayo, arena gruesa y gravilla de la cantera “Los Mellizos”, una relación agua/cemento constante de 0.62. La caracterización de los agregados naturales y de los residuos de botellas de plástico PET así como de caucho de llantas recicladas se realizaron bajo las Normas Técnicas Peruanas: contenido de humedad (NTP 399.185), peso específico y absorción (NTP 400.022 y NTP 400.021), peso unitario (NTP 400.017) y granulometría (NTP 400.012). Se conformaron probetas cilíndricas de 15 cm de diámetro y 30 cm de alto; curadas en una poza de agua con hidróxido de calcio (NTP 339.183). Para determinar su resistencia a la compresión se empleó la norma NTP 339.034. Los resultados obtenidos fueron: Probeta patrón 0% de sustitución: 128.26 (Kg/cm²), 163.71 (Kg/cm²), 172.69 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente. Con 5% de caucho: 97.00 (Kg/cm²), 134.16 (Kg/cm²), 140.04 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente. Probeta con 10% de caucho: 72.81 (Kg/cm²), 80.15 (Kg/cm²), 118.90 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente. Con 15% de sustitución de caucho 45.80 (Kg/cm²), 64.17 (Kg/cm²), 86.62 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente. Con 5% de plástico PET: 125.96 (Kg/cm²), 153.51 (Kg/cm²), 163.24 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente. Probeta con 10% de plástico PET: 87.47 (Kg/cm²), 137.97 (Kg/cm²), 150.76 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente. Con 15% de sustitución de plástico PET 72.29 (Kg/cm²), 111.47 (Kg/cm²), 137.26 (Kg/cm²); a los 7, 14 y 28 días de curado respectivamente.
Mostrar más
 
The objective of the present investigation was to calculate the influence on the compressive strength of conventional concrete, replacing fine aggregate with PET plastic and recycled rubber. The replacement is in volume at 0%, 5%, 10% and 15% For this, a standard mix design was made to obtain a conventional concrete of 175 kg / cm², based on Composite Portland Cement Type I Co from Pacasmayo, coarse sand and gravel from the "Los Mellizos" quarry, a water cement ratio constant of 0.62. The characterization of the natural aggregates and waste from PET plastic bottles as well as rubber from recycled tires were carried out under the Peruvian Technical Standards: moisture content (NTP 399.185), specific weight and absorption (NTP 400.022 and NTP 400.021), unit weight (NTP 400.017) and granulometry (NTP 400.012). Cylindrical specimens of 15 cm in diameter and 30 cm in height were formed; cured in a pool of water with calcium hydroxide (NTP 339.183). To determine its compressive strength, the NTP 339.034 standard was used. The results obtained were: 0% substitution test sample: 128.26 (Kg / cm²), 163.71 (Kg / cm²), 172.69 (Kg / cm²); at 7, 14 and 28 days of curing respectively. With 5% rubber: 97.00 (Kg / cm²), 134.16 (Kg / cm²), 140.04 (Kg / cm²); at 7, 14 and 28 days of curing respectively. Test tube with 10% rubber: 72.81 (Kg / cm²), 80.15 (Kg / cm²), 118.90 (Kg / cm²); at 7, 14 and 28 days of curing respectively. With 15% rubber replacement 45.80 (Kg / cm²), 64.17 (Kg / cm²), 86.62 (Kg / cm²); at 7, 14 and 28 days of curing respectively. With 5% PET plastic: 125.96 (Kg / cm²), 153.51 (Kg / cm²), 163.24 (Kg / cm²); at 7, 14 and 28 days of curing respectively. Test tube with 10% PET plastic: 87.47 (Kg / cm²), 137.97 (Kg / cm²), 150.76 (Kg / cm²); at 7, 14 and 28 days of curing respectively. With 15% PET plastic replacement 72.29 (Kg / cm²), 111.47 (Kg / cm²), 137.26 (Kg / cm²); at 7, 14 and 28 days of curing respectively.
Mostrar más
 
URI
https://hdl.handle.net/11537/13597
Bibliographic citation
Miranda, J. L., & Quispe, A. A. (2018). Influencia en la resistencia a la compresión del concreto convencional al sustituir agregado fino por plástico Pet y caucho de llantas recicladas [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. Recuperado de https://hdl.handle.net/11537/13597
Subject
Resistencia a la comprensión
Resistencia de materiales
Concreto
Collections
  • Tesis [1081]

Related items

Showing items related by title, author, creator and subject.

  • Thumbnail

    Resistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto reciclado 

    Rodríguez Cabanillas, Gianmarco (Universidad Privada del Norte, 2018-09-05)
    Acceso abierto
    RESUMEN La presente tesis tiene como objetivo determinar la resistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto reciclado. Para este estudio se utilizó ...
  • Thumbnail

    Permeabilidad de un concreto F’C = 210 KG/CM2 utilizando diferentes porcentajes de aditivo plastificante, Cajamarca, 2016 

    Abanto Cabellos, Tatiana Enet (Universidad Privada del Norte, 2016-10-29)
    Acceso abierto
    RESUMEN El concreto es un material que se utiliza en la construcción de diferentes tipos de edificaciones, en muchos casos se recomienda el uso de aditivos, para mejorar algunas propiedades del concreto, entre una de ...
  • Thumbnail

    Efecto de tres niveles de PET reciclado como reemplazo de agregado fino en la resistencia a compresión axial del concreto convencional f’c 210 kg/cm2 

    Cholán De La Cruz, Julio Ulises (Universidad Privada del Norte, 2018-01-05)
    Acceso abierto
    La presente investigación tiene como objetivo determinar la resistencia a compresión axial reemplazando el agregado fino por PET reciclado en 5%, 10% y 15% en un concreto convencional f’c = 210 kg/cm según la NTP ...

Contacto:  [email protected]

  • Estadísticas
  • English 
    • español
    • English
  • Login

Todos los derechos reservados.
 

 

Documentos
Política del Repositorio Institucional UPN

Browse

All of DSpaceCommunities & CollectionsBy Issue DateAuthorsAdvisorsTitlesSubjectsVenuesTypes of researchThis CollectionBy Issue DateAuthorsAdvisorsTitlesSubjectsVenuesTypes of research

Contacto:  [email protected]

  • Estadísticas
  • English 
    • español
    • English
  • Login

Todos los derechos reservados.