dc.contributor.advisorVásquez Alfaro, Iván Eugenio
dc.contributor.authorVaras Bermudez, Geiby Natieli
dc.date.accessioned2018-08-22T20:19:09Z
dc.date.available2018-08-22T20:19:09Z
dc.date.issued2018-05-23
dc.identifier.citationVaras, G. N. (2018). Influencia de los tipos de cal y proporción en morteros para la conservación sobre la compresión, contracción, densidad, absorción y fraguado, Trujillo 2018 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. Recuperado de https://hdl.handle.net/11537/13747es_PE
dc.identifier.other624.1834 VARA 2018es_PE
dc.identifier.urihttps://hdl.handle.net/11537/13747
dc.description.abstractSe han realizado desde los tiempos de la colonia, intervenciones estructurales y no estructurales ya sea por reconstrucción de partes colapsadas, reparaciones o colocación de refuerzos sísmicos, el paso del tiempo y nuevas construcciones. Por ello, la presente investigación plantea la utilización de cal en morteros de asiento con adicionamiento de arena como alternativa para mejorar sus propiedades físicas y mecánicas para restauraciones y mantenimiento de estructuras coloniales. Para el desarrollo se utilizó arena grano grueso con módulo de finura de 2.5 ; cal Martell, Hades, Informal I, Informal II, Informal III e Informal IV, con agua constante y con dosificaciones de reemplazo de cal por arena de 100%:0, 90%:10%, 80%:20%, 70%:30% y 60%:40%; tanto la relación agua/cal como los porcentajes de reemplazo fueron asignados por un estudio preliminar a la investigación; las probetas aproximadamente de 28 días de curado fueron sometidas a diferentes ensayos. Se desarrollaron los ensayos de caracterización del agregado y de la cal como granulometría por lavado (NTP 400.018), contenido de humedad (NTP 339.185), peso específico y absorción (NTP 400.022), peso unitario suelto seco y peso unitario seco compactado (NTP 400.017). También los ensayos físicos en estado endurecido del mortero que fueron densidad, absorción (ASTM C 373), tiempo de fraguado (ASTM C 191) y contracción (UNE – 80-112), ensayos mecánicos como la resistencia a la compresión (NTP 400.051). Se elaboraron 450 probetas cúbicas de 5cm x 5cm x5cm. Se determinó que estos morteros no servirían estructuralmente , pero así mismo la dosificación más óptima del estudio fue la de 100%:0% con la cal hades, pues se pudo observar una mezcla plástica, trabajable y morteros con baja porosidad con una resistencia máxima de 22 kg/cm2 , densidad de 1448 kg/m3 ,absorción de 22%, un tiempo de fraguado de 540 minutos con una temperatura de 22.3 °C y se contrae 2.4 %;mientras que la dosificación que presento valores mínimos fue la de dosificación 60%:40% en cal informal IV ,con una resistencia de 2 kg/cm2 , densidad de 1143 kg/m3 , absorción de 40 %, tiempo de fraguado de 3960 minutos con una temperatura de 19.5 °C y una expansión de 7.1 %.Finalmente se puede decir que la dosificación 100%:0% con el uso de la cal hades ayudaría a mejorar las condiciones de los morteros para emplearlos en el mantenimiento y conservación de estructuras coloniales, de esa manera conservar la esencia de los materiales de construcción empleados por nuestros antepasados.es_PE
dc.description.abstractSince the time of the colony, structural and non-structural interventions have been carried out either by reconstruction of collapsed parts, repairs or seismic reinforcement placement, the passage of time and new constructions. For this reason, the present investigation proposes the use of lime in seat mortars with the addition of sand as an alternative to improve its physical and mechanical properties for restorations and maintenance of colonial structures. For the development, coarse-grained sand with a fineness modulus of 2.5 was used; Cal Martell, Hades, Informal I, Informal II, Informal III and Informal IV, with constant water and with lime replacement dosages per 100% sand: 0, 90%: 10%, 80%: 20%, 70%: 30% and 60%: 40%; both the water / lime ratio and the replacement percentages were assigned by a preliminary study to the investigation; the test pieces approximately 28 days of curing were subjected to different tests. The aggregate and lime characterization tests were developed as washing granulomere (NTP 400.018), moisture content (NTP 339.185), specific gravity and absorption (NTP 400.022), dry loose unit weight and compacted dry unit weight (NTP 400.017). Also the physical tests in the hardened state of the mortar that were density, absorption (ASTM C 373), setting time (ASTM C 191) and shrinkage (UNE - 80-112), mechanical tests such as compressive strength (NTP 400.051) . 450 cubic samples of 5cm x 5cm x5cm were prepared. It was determined that these mortars would not serve structurally, but also the most optimal dosage of the study was 100%: 0% with cal hades, because it was possible to observe a plastic, workable mixture and mortars with low porosity with a maximum resistance of 22 kg / cm2 , density of 1448 kg / m3 , absorption of 22%, a setting time of 540 minutes with a temperature of 22.3 °C and shrinks 2.4%;while the dosage that presented minimum values was the 60% dosage: 40% in informal lime IV, with a resistance of 2 kg / cm2, density of 1143 kg / m3 , absorption of 40%, setting time of 3960 minutes with a temperature of 19.5 °C and an expansion of 7.1%.Finally, it can be said that the 100%: 0% dosage with the use of lime hades would help to improve the conditions of the mortars to be used in the maintenance and conservation of colonial structures, in this way to preserve the essence of the construction materials used by our ancestors.es_PE
dc.description.uriTesises_PE
dc.formatapplication/pdfes_PE
dc.language.isospaes_PE
dc.publisherUniversidad Privada del Nortees_PE
dc.rightsinfo:eu-repo/semantics/openAccesses_PE
dc.rightsAtribución-NoComercial-CompartirIgual 3.0 Estados Unidos de Américaes_PE
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/3.0/us/*
dc.sourceUniversidad Privada del Nortees_PE
dc.sourceRepositorio Institucional - UPNes_PE
dc.subjectMateriales de construcciónes_PE
dc.subjectResistencia a la compresiónes_PE
dc.subjectArenaes_PE
dc.titleInfluencia de los tipos de cal y proporción en morteros para la conservación sobre la compresión, contracción, densidad, absorción y fraguado, Trujillo 2018es_PE
dc.typeinfo:eu-repo/semantics/bachelorThesises_PE
thesis.degree.grantorUniversidad Privada del Norte. Facultad de Ingenieríaes_PE
thesis.degree.levelTítulo Profesionales_PE
thesis.degree.disciplineIngeniería Civiles_PE
thesis.degree.nameIngeniero Civiles_PE
dc.publisher.countryPEes_PE
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.01.01es_PE
thesis.degree.programPregradoes_PE
dc.description.sedeTrujillo San Isidroes_PE
renati.advisor.dni80524374
renati.advisor.orcidhttps://orcid.org/0000-0002-6717-0501es_PE
renati.author.dni70509871
renati.discipline732016es_PE
renati.jurorVillar Quiroz, Josualdo Carlos
renati.jurorAzañedo Medina, Wiston Henry
renati.jurorAvalos Alayo, Ricardo Daniel
renati.levelhttps://purl.org/pe-repo/renati/level#tituloProfesionales_PE
renati.typehttp://purl.org/pe-repo/renati/type#tesises_PE


Files in this item

Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess