dc.identifier.citationCastañeda, R. E. (2018). Influencia de la adición de fibra de acero y plastificante en la resistencia a la compresión del concreto convencional, Trujillo -2018 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. Recuperado de https://hdl.handle.net/11537/13800es_PE
dc.identifier.other624.18341 CAST 2018es_PE
dc.identifier.urihttps://hdl.handle.net/11537/13800
dc.description.abstractLa investigación realizada se centra en el análisis de la influencia de la fibra de acero y aditivo plastificante en la resistencia a la compresión de un concreto convencional. Las dosificaciones de la fibra de acero que se trabajó fueron dos, de 20 kg/m3 y 40 kg/m3. Para el desarrollo de este trabajo, se elaboró un diseño de mezcla considerando los criterios de diseño para una resistencia a esfuerzo de comprensión de 210 kg/cm2, siguiendo la metodología del método ACI 211. Seguidamente se llevó a cabo el ensayo de resistencia a la compresión, pudiendo así, evaluar y comparar el comportamiento de las distintas dosificaciones de fibra de acero reflejado en esta investigación. De los resultados obtenidos, se determinó que el concreto convencional se obtuvo para una edad de curado de 7 días; una resistencia a la compresión promedio de 171.40 kg/cm2 para el concreto patrón, una resistencia promedio de 181.00 kg/cm2 para el concreto con adición de 20 kg/m3 de fibra de acero; y una resistencia promedio de 184.10 kg/cm2 para el concreto con adición de 40 kg/m3 de fibra de acero. Para una edad de curado de 14 días; una resistencia a la compresión promedio de 198.20 kg/cm2 para el concreto patrón, una resistencia promedio de 210.70 kg/cm2 para el concreto con adición de 20 kg/m3 de fibra de acero; y una resistencia promedio de 211.60 kg/cm2 para el concreto con adición de 40 kg/m3 de fibra de acero. Para una edad de curado de 28 días; una resistencia a la compresión promedio de 220.40 kg/cm2 para el concreto patrón, una resistencia promedio de 230.60 kg/cm2 para el concreto con adición de 20 kg/m3 de fibra de acero; y una resistencia promedio de 238.90 kg/cm2 para el concreto con adición de 40 kg/m3 de fibra de acero. Obteniendo así una confianza mayor al 95%. Se concluye que se logró un incremento de la resistencia a la compresión del concreto que asciende en 4.63% (C.P + 20kg/m3) y 8.39% (C.P + 40 kg/m3), consecuentemente expreso una comprobada recomendación para el incremento de la resistencia a la compresión y evitar un concreto con deficiencias en su resistencia.es_PE
dc.description.abstractThe research carried out focuses on the analysis of the influence of steel fiber and plasticizer additive on the compressive strength of a conventional concrete. The dosages of the steel fiber that was worked on were two, of 20 kg / m3 and 40 kg / m3. For the development of this work, a mix design was developed for the analysis of the design criteria for an effort resistance of 210 kg / cm2, following the methodology of the ACI 211 method. The resistance test was then carried out the compression, thus being able to evaluate and compare the behavior of the different dosages of steel fiber reflected in this investigation. From the results obtained, it was determined that conventional concrete was obtained for a cure age of 7 days; an average compressive strength of 171.40 kg / cm2 for the concrete standard, an average strength of 181.00 kg / cm2 for concrete with the addition of 20 kg / m3 of steel fiber; and an average resistance of 184.10 kg / cm2 for concrete with addition of 40 kg / m3 of steel fiber. For a curing age of 14 days; an average compressive strength of 198.20 kg / cm2 for the concrete standard, an average strength of 210.70 kg / cm2 for concrete with the addition of 20 kg / m3 of steel fiber; and an average strength of 211.60 kg / cm2 for concrete with the addition of 40 kg / m3 of steel fiber. For a cure age of 28 days; an average compressive strength of 220.40 kg / cm2 for the concrete standard, an average strength of 230.60 kg / cm2 for concrete with the addition of 20 kg / m3 of steel fiber; and an average resistance of 238.90 kg / cm2 for concrete with the addition of 40 kg / m3 of steel fiber. Obtaining thus a confidence greater than 95%. It is concluded that an increase in the compressive strength of the concrete was achieved, amounting to 4.63% (CP + 20kg / m3) and 8.39% (CP + 40 kg / m3), consequently expressed a proven recommendation for the increase of the resistance to compression and avoid a concrete with deficiencies in its resistance.es_PE
dc.description.uriTesises_PE
dc.formatapplication/pdfes_PE
dc.formatapplication/mswordes_PE
dc.language.isospaes_PE
dc.publisherUniversidad Privada del Nortees_PE
dc.rightsinfo:eu-repo/semantics/openAccesses_PE
dc.rightsAtribución-NoComercial-CompartirIgual 3.0 Estados Unidos de Américaes_PE
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/3.0/us/*
dc.sourceUniversidad Privada del Nortees_PE
dc.sourceRepositorio Institucional - UPNes_PE
dc.subjectConcretoes_PE
dc.subjectResistencia a la comprensiónes_PE
dc.subjectAceroes_PE
dc.titleInfluencia de la adición de fibra de acero y plastificante en la resistencia a la compresión del concreto convencional, Trujillo -2018es_PE
dc.typeinfo:eu-repo/semantics/bachelorThesises_PE
thesis.degree.grantorUniversidad Privada del Norte. Facultad de Ingenieríaes_PE
thesis.degree.levelTítulo Profesionales_PE
thesis.degree.disciplineIngeniería Civiles_PE
thesis.degree.nameIngeniero Civiles_PE
dc.publisher.countryPEes_PE
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.01.01es_PE
thesis.degree.programPregradoes_PE
dc.description.sedeTrujillo San Isidroes_PE
renati.advisor.dni41526075
renati.advisor.orcidhttps://orcid.org/0000-0003-1737-3500es_PE
renati.author.dni74285572
renati.discipline732016es_PE
renati.jurorVillar Quiroz, Josualdo
renati.jurorAguilar Villena, Roxana
renati.jurorVásquez Diaz, Alberto Rubén
renati.levelhttps://purl.org/pe-repo/renati/level#tituloProfesionales_PE
renati.typehttp://purl.org/pe-repo/renati/type#tesises_PE


Files in this item

Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess