dc.identifier.citationRodrígue, G. (2018). Resistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto reciclado (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de http://hdl.handle.net/11537/13841es_PE
dc.identifier.otherTES 624 RODR/R 2018
dc.identifier.urihttps://hdl.handle.net/11537/13841
dc.description.abstractRESUMEN La presente tesis tiene como objetivo determinar la resistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto reciclado. Para este estudio se utilizó agregados de la cantera Roca Fuerte, cemento Portland tipo MS (MH) (R) y bloques de concreto recolectados de un botadero los cuales fueron triturados en la cantera Roca Fuente; se inició evaluando las propiedades físicas y mecánicas de los agregados naturales y reciclados en los laboratorios Ingeniería Civil de la Universidad Privada del Norte, determinando que su granulometría está dentro de los límites de acuerdo a la norma ASTM C-33. Consecuentemente se realizó el diseño con agregados de concreto reciclado y agregados naturales para un f’c=175 Kg/cm2 utilizando la metodología combinación de agregados evaluados en tres periodos de curado 7 ,14 ,28 días de edad. Los resultados obtenidos en el laboratorio de la UPN indicaron que a 7 días de curado la resistencia promedio alcanzada fue de 163.17 kg/cm² con agregado natural 100%; 141.87 kg/cm² al reemplazar 50% de agregados de concreto reciclado, 129.86 kg/cm² al reemplazar 75% de agregados de concreto reciclado y 96.37 kg/cm² con un 100% de agregados de concreto reciclado; para un tiempo de curado de 14 días la resistencia promedio alcanzada fue de 224.33 kg/cm² con agregado natural 100%; 175.61 kg/cm² al reemplazar 50% de agregados de concreto reciclado, 163.63 kg/cm² al reemplazar 75% de agregados de concreto reciclado y 150.11 kg/cm² con un 100% de agregados de concreto reciclado; así mismo en un tiempo de curado de 28 días la resistencia promedio alcanzada fue de 252.60 kg/cm² con agregado natural 100%; 205.88 kg/cm² al reemplazar 50% de agregados de concreto reciclado, 191.24 kg/cm² al reemplazar 75% de agregados de concreto reciclado y por último 186.35 kg/cm² con un 100% de agregados de concreto reciclado. Concluyendo que al reemplazar concreto reciclado por agregados la resistencia disminuye para los para 7 días hasta 40.94%, a los 14 días hasta 33.09% y a los 28 días hasta 26.23% con respecto a la resistencia de la probeta patrón; no se cumple la hipótesis planteada ya que según los resultados la resistencia disminuye proporcionalmente al aumento del porcentaje de concreto reciclado utilizado.es_PE
dc.description.abstractABSTRACT The objective of this thesis is to determine the compressive strength of concrete f'c = 175 kg / cm2 with three percentages of replacement of aggregates with recycled concrete. For this study, aggregates from the Roca Fuerte quarry, MS type cement (MH) (R) and concrete blocks collected from a dump were used, which were crushed at the Roca Fuente quarry; It was started evaluating the physical and mechanical properties of the natural and recycled aggregates in the Civil Engineering laboratories of the Universidad Privada del Norte, determining that its granulometry is within the limits according to the ASTM C-33 standard. Consequently, the design was made with aggregates of recycled concrete and natural aggregates for a f'c = 175 Kg / cm2 using the combination methodology of aggregates evaluated in three curing periods 7, 14, 28 days of age. The results obtained in the UPN laboratory indicated that after 7 days of curing the average resistance reached was 163.17 kg / cm² with natural aggregate 100%; 141.87 kg / cm² by replacing 50% of aggregates of recycled concrete, 129.86 kg / cm² by replacing 75% of aggregates of recycled concrete and 96.37 kg / cm² with 100% of aggregates of recycled concrete; for a curing time of 14 days the average resistance reached was 224.33 kg / cm² with 100% natural aggregate; 175.61 kg / cm² when replacing 50% of aggregates of recycled concrete, 163.63 kg / cm² when replacing 75% of aggregates of recycled concrete and 150.11 kg / cm² with 100% of aggregates of recycled concrete; Likewise, in a curing time of 28 days, the average resistance reached was 252.60 kg / cm² with 100% natural aggregate; 205.88 kg / cm² when replacing 50% of aggregates of recycled concrete, 191.24 kg / cm² when replacing 75% of aggregates of recycled concrete and finally 186.35 kg / cm² with 100% of aggregates of recycled concrete. Concluding that when replacing recycled concrete with aggregates, the resistance decreases for those for 7 days up to 40.94%, at 14 days up to 33.09% and at 28 days up to 26.23% with respect to the strength of the standard specimen; the hypothesis is not fulfilled since according to the results the resistance decreases proportionally to the increase of the percentage of recycled concrete used.es_PE
dc.description.uriTesisspa
dc.formatapplication/pdf
dc.language.isospaes_PE
dc.publisherUniversidad Privada del Nortees_PE
dc.rightsinfo:eu-repo/semantics/openAccesses_PE
dc.sourceUniversidad Privada del Nortees_PE
dc.sourceRepositorio Institucional - UPNes_PE
dc.subjectConcretoes_PE
dc.subjectResistencia a la compresiónes_PE
dc.subjectPavimentos
dc.titleResistencia a la compresión del concreto f’c=175 kg/cm2 con tres porcentajes de reemplazo de agregados con concreto recicladoes_PE
dc.typeinfo:eu-repo/semantics/bachelorThesises_PE
thesis.degree.grantorUniversidad Privada del Norte. Facultad de Ingenieríaspa
thesis.degree.levelIngenierospa
thesis.degree.disciplineIngeniería Civilspa
thesis.degree.nameIngeniero Civilspa
dc.publisher.countryPEes_PE
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.01.01
dc.description.sedeCajamarca
renati.discipline732016


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record