dc.contributor.advisorVásquez Díaz, Alberto Rubén
dc.contributor.authorCruz Garcia, Hilder
dc.date.accessioned2019-05-10T14:26:21Z
dc.date.available2019-05-10T14:26:21Z
dc.date.issued2019-04-16
dc.identifier.citationCruz, H. (2019). Influencia de cenizas de ladrillos artesanales en la resistencia a la compresión de adoquines de concreto, Trujillo 2019 (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de http://hdl.handle.net/11537/21165es_PE
dc.identifier.other624.1836 CRUZ 2019es_PE
dc.identifier.urihttps://hdl.handle.net/11537/21165
dc.description.abstractLa presente investigación se realizó en Trujillo, en la Universidad Privada del Norte, tiene como finalidad determinar la influencia del porcentaje de cenizas de ladrillos artesanales en la resistencia a la compresión de adoquines tipo II; reduciendo de tal manera costos y la contaminación ambiental. Para la realización de la tesis se utilizó un diseño experimental puro, el muestreo fue probabilístico utilizando como antecedentes estudios anteriores de adoquines de concreto, la recolección de datos se realizó con la técnica de la observación, el instrumento utilizado fue la guía de observaciones, para analizar los datos se empleó a la inferencia estadístico. Está investigación se basó en muestras de probetas de adoquines de concreto, las cuales fueron elaborados con cemento MS, agregado fino y grueso de la cantera el Milagro. De los resultados obtenidos se determinó los promedios para cada adición que fueron los siguientes, con 5%, 10%, 15%, 20% y 25% se realizaron 9 probetas por adición, 3 ensayadas a los 3 días, 7 días y 28 días, también se evaluó el porcentaje de absorción utilizando 3 probetas por adición. Finalmente se determinó que el promedio de adoquines con 10 % de cenizas de ladrillos artesanales presenta una mayor resistencia a los 28 días de curado de 385.29 kg/cm2, por otro lado el promedio de los adoquines con 15 % de adición superan la resistencia de 340 kg/cm2 que señala la NTP 399.611, por la cual también pueden ser utilizados. La investigación concluye que los adoquines con 10% de adición de cenizas de ladrillos artesanales tienen mayor influencia en la resistencia a la compresión de adoquines de concreto tipo II para uso de vehículos ligeros.es_PE
dc.description.abstractThe present investigation was carried out in Trujillo, at the Universidad Privada del Norte, aims to determine the influence of the percentage of ashes of artisanal bricks on the compressive strength of type II paving stones; thereby reducing costs and environmental pollution. For the realization of the thesis a pure experimental design was used, the sampling was probabilistic using as background previous studies of concrete pavers, the data collection was done with the technique of observation, the instrument used was the observation guide, to analyze the data, statistical inference was used. This research was based on samples of concrete pavers, which were made with MS cement, fine and coarse aggregate from El Milagro quarry. From the results obtained, the averages for each addition were determined, which were the following, with 5%, 10%, 15%, 20% and 25% 9 samples were made by addition, 3 tested at 3 days, 7 days and 28 days, the percentage of absorption was also evaluated using 3 samples per addition. Finally, it was determined that the average of paving stones with 10% of ashes of handmade bricks presents a greater resistance to the 28 days of curing of 385.29 kg / cm2, on the other hand, the average of the paving stones with 15% addition exceed the resistance of 340 kg / cm2 indicated by the NTP 399.611, by which they can also be used. The research concludes that paving stones with 10% addition of artisan brick ash have a greater influence on the compressive strength of type II concrete pavers for the use of light vehicles.es_PE
dc.description.uriTesises_PE
dc.formatapplication/pdfes_PE
dc.formatapplication/mswordes_PE
dc.language.isospaes_PE
dc.publisherUniversidad Privada del Nortees_PE
dc.rightsinfo:eu-repo/semantics/openAccesses_PE
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/2.5/pe/*
dc.sourceUniversidad Privada del Nortees_PE
dc.sourceRepositorio Institucional - UPNes_PE
dc.subjectConcreto /Hormigónes_PE
dc.subjectLadrilloes_PE
dc.subjectEstructurases_PE
dc.subjectResistencia a la compresión
dc.subjectLadrillo
dc.titleInfluencia de cenizas de ladrillos artesanales en la resistencia a la compresión de adoquines de concreto, Trujillo 2019es_PE
dc.typeinfo:eu-repo/semantics/bachelorThesises_PE
thesis.degree.grantorUniversidad Privada del Norte. Facultad de Ingenieríaes_PE
thesis.degree.levelTítulo Profesionales_PE
thesis.degree.disciplineIngeniería Civiles_PE
thesis.degree.nameIngeniero Civiles_PE
dc.publisher.countryPEes_PE
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.01.01es_PE
thesis.degree.programPregradoes_PE
dc.description.sedeTrujillo San Isidroes_PE
renati.advisor.dni40385695
renati.advisor.dni70875311
renati.advisor.orcidhttps://orcid.org/0000-0001-9018-5763
renati.discipline732016es_PE
renati.levelhttps://purl.org/pe-repo/renati/level#tituloProfesionales_PE
renati.typehttps://purl.org/pe-repo/renati/type#tesises_PE


Ficheros en el ítem

Thumbnail
Thumbnail
Thumbnail

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem

info:eu-repo/semantics/openAccess
Excepto si se señala otra cosa, la licencia del ítem se describe como info:eu-repo/semantics/openAccess