dc.identifier.citationMinaya, M. N. (2020). Influencia de la incorporación de fibra de coco para la incidencia en la resistencia del concreto F’C=210 KG/CM2 – Lima 2020 (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de https://hdl.handle.net/11537/25036es_PE
dc.identifier.other620.1124 MINA 2020es_PE
dc.identifier.urihttps://hdl.handle.net/11537/25036
dc.description.abstractEl presente trabajo de investigación tuvo como objetivo demostrar en qué medida la incorporación de la fibra de coco incide en la resistencia en el concreto F'c=210 kg/cm2, por lo cual se considera una investigación de diseño cuasiexperimental, con nivel explicativo. Las bases de datos usados fueron de Redalyc. Se realizó la caracterización de los agregados grueso y fino, los agregados provienen de la cantera de Jicamarca (UNICON). Los ensayos fueron realizados para determinar el diseño de mezcla con el método de Bolomey. La fibra de coco fue obtenida en el Mercado de fruta N°01, el volumen de fibra de coco que fue utilizado 0%,1.5% y 2.0%, fueron añadidos en la mezcla en relación del cemento. En la cual se efectuaron 27 muestras de probetas para tracción, 27 muestras de probetas para compresión y 27 muestras de vigas para flexión ; en resistencia a la compresión incorporando 1.5% de fibra de coco incrementa la resistencia en 28% a los convencionales; como resultado la mezcla que presentó mayor resistencia a la tracción diametral en las probetas convencionales fue la que contenía 2.0% de fibra de coco incrementando su resistencia 20%; el diseño de mezcla que presento resistencia a la flexión con carga en los puntos tercios a mayor respecto a las vigas convencionales fue del 2.0% de fibra de coco incrementando su resistencia en 15% del concreto convencional. Con dichos resultados podemos concluir que el 2.0% de fibra de coco incrementa las propiedades mecánicas del concreto. En esta tesis no sé presento ninguna limitación al momento de realizar el estudio.es_PE
dc.description.abstractThe objective of this research work was to demonstrate to what extent the incorporation of coconut fiber affects resistance in concrete F'c = 210 kg / cm2, which is why it is considered a quasi-experimental design research, with an explanatory level. The databases used were from Redalyc. The characterization of the coarse and fine aggregates was carried out, the aggregates come from the Jicamarca quarry (UNICON). The tests were carried out to determine the mix design with the Bolomey method. The coconut fiber was obtained in the Fruit Market No. 01, the volume of coconut fiber that was used 0%, 1.5% and 2.0%, was added to the mix in relation to the cement. In which 27 samples of specimens for traction, 27 samples of specimens for compression and 27 samples of beams for flexion were made; in compression resistance incorporating 1.5% coconut fiber increases the resistance by 28% to conventional ones; As a result, the mixture that presented the greatest resistance to diametric traction in conventional test tubes was the one that contained 2.0% coconut fiber, increasing its resistance by 20%; The mix design that presented resistance to bending with load at the thirds point higher than conventional beams was 2.0% coconut fiber, increasing its resistance by 15% of conventional concrete. With these results we can conclude that 2.0% of coconut fiber increases the mechanical properties of concrete. In this thesis, I do not know of any limitations at the time of the study.es_PE
dc.description.uriTesises_PE
dc.formatapplication/pdfes_PE
dc.formatapplication/mswordes_PE
dc.language.isospaes_PE
dc.publisherUniversidad Privada del Nortees_PE
dc.rightsinfo:eu-repo/semantics/embargoedAccesses_PE
dc.sourceUniversidad Privada del Nortees_PE
dc.sourceRepositorio Institucional - UPNes_PE
dc.subjectFibras vegetaleses_PE
dc.subjectResistencia a la compresiónes_PE
dc.subjectMateriales de construcciónes_PE
dc.titleInfluencia de la incorporación de fibra de coco para la incidencia en la resistencia del concreto F’C=210 KG/CM2 – Lima 2020es_PE
dc.typeinfo:eu-repo/semantics/bachelorThesises_PE
thesis.degree.grantorUniversidad Privada del Norte. Facultad de Ingenieríaes_PE
thesis.degree.levelTítulo Profesionales_PE
thesis.degree.disciplineIngeniería Civiles_PE
thesis.degree.nameIngeniero Civiles_PE
dc.publisher.countryPEes_PE
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.01.01es_PE
thesis.degree.programPregradoes_PE
dc.description.sedeLos Olivoses_PE
renati.advisor.dni08644876
renati.advisor.orcidhttps://orcid.org/0000-0002-5043-6510es_PE
renati.author.dni74068236
renati.discipline732016es_PE
renati.jurorPoma Zumarán, Aldo Juan
renati.jurorQuesada Llanto, Julio Christian
renati.jurorVildoso Flores, Alejandro
renati.levelhttps://purl.org/pe-repo/renati/level#tituloProfesionales_PE
renati.typehttps://purl.org/pe-repo/renati/type#tesises_PE


Files in this item

Thumbnail
Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record